Product Details:
|
| Place Of Origin: | Beijing, China | Brand Name: | Spark |
|---|---|---|---|
| Type: | Bare | Application: | Heating, Casting |
| Conductor Material: | Fe-Cr-Al | Conductor Type: | Solid |
| Insulation Material: | Rubber | Name: | 0Cr20Al6 |
| Brand: | SPARK | Standard: | GB/T 1234-2012 |
| Package: | Wooden Case | MOQ: | 500 Kilograms |
| Delivery Time: | 15-20 Days | Color: | Silver Gray |
| Certificate: | ISO9001 | Shape: | Lump |
Products Description
Nowadays,induction cookers and traditional light wave cookers have become main electrical stove in kitchens. Induction cookers can't continuously work on the condition of small fire, with which the electromagnetic wave harmful for people is radiated.Because of the low heat quantity applied by traditional light wave cookers,their temperature rise too slowly to fry quickly and waste too much energy. To make up for the deficiency of cooker, a new cooker product for advanced glass top hot plates has been developed at home and abroad.
As a professional company researching the electrical heating alloy,we have designed special thin wide strip for heating components of glass top hot plates.
Steel grades and Chemical composition
|
Steel grades |
Chemical composition% |
||||||
|
C |
Si |
Cr |
Al |
S |
P |
rare earth element |
|
|
0Cr20Al6 |
≤0.03 |
≤0.4 |
19-21 |
5.0-6.0 |
≤0.02 |
≤0.025 |
Appropriate amount |
Size range
Thickness:0.04-0.1mm±4%
Width:5-120mm±0.0.5mm
Properties
|
Steel grades |
Maximum service temperature |
tensile strength(N/mm²) |
Elongation% |
Electrical resistivity |
|
0Cr20Al6 |
1300℃ |
650-800 |
>12 |
1.45±0.05 |
Based on good plasticity of the alloys,they have excellent cold working formability. The alloys' resistance fluctuation is small,and the value of resistance per meter is no higher than four percent, which cause that the alloys are beneficial in even heating. The trace element addedin the alloys promote oxide film fixed with the body to form in heating process, that improve the alloys' oxidation resistance at elevated temperature. With the help of trace element, creep resistance is greatly improved at high temperature. The products have not being deformed after elevated temperature for a long time.
production process
Raw material factory Smelt steel roll
detection Winding Annealing drawing